産品詳細介紹 |
項 目 \ 牌 号 |
高(gāo)鋁質 |
粘土質 |
剛玉質莫來(lái)石質
|
鎂質 |
LN-55A |
LN-55B |
LN-65A |
LN-65B |
LN-75A |
LN-75B |
LN-85B |
GN-85B |
NN-30 |
NN-38 |
NN-42 |
NN-45A |
NN-45B |
AM-90 |
MS-80 |
MS-60 |
MF-93 |
MF-82 |
MF-78 |
Al2O3 % |
≥55 |
≥55 |
≥65 |
≥65 |
≥75 |
≥75 |
≥85 |
≥85 |
≥30 |
≥38 |
≥42 |
≥45 |
≥45 |
≥90 |
≥80 |
≥60 |
|
|
|
耐火(huǒ)度 ℃ |
≥1770 |
≥1770 |
≥1790 |
≥1790 |
≥1790 |
≥1790 |
≥1790 |
≥1790 |
≥1630 |
≥1690 |
≥1710 |
≥1730 |
≥1730 |
≥1790 |
≥1790 |
≥1770 |
灼減 ≤2.0 |
荷重軟化溫T2℃ |
|
≥1300 |
|
≥1400 |
|
≥1400 |
|
≥1650 |
|
|
|
|
≥1200 |
≥1600 |
≥1500 |
≥1400 |
MgO % ≥93 |
MgO % ≥82 |
MgO % ≥78
|
抗折強度 MPa
|
110℃×24h |
≥1.0 |
≥2.0 |
≥1.0 |
≥2.0 |
≥1.0 |
≥2.0 |
≥2.0 |
≥2.0 |
≥1.0 |
≥1.0 |
≥1.0 |
≥1.0 |
≥2.0 |
≥2.5 |
≥3.0 |
≥2.0 |
SiO2 % ≤2.2 |
SiO2 % ≤9.0 |
|
1200℃×3h |
|
|
|
|
|
|
|
|
≥3.0 |
≥3.0 |
≥3.0 |
≥3.0 |
≥6.0 |
|
|
|
|
1400℃×3h |
≥3.0 |
≥6.0 |
≥3.0 |
≥6.0 |
≥3.0 |
≥6.0 |
|
|
|
|
|
|
|
|
|
|
1500℃×3h |
|
|
|
|
|
|
≥6.0 |
≥6.0 |
|
|
|
|
|
≥6 |
≥6 |
≥6 |
燒後線 變化率 % |
1500℃×3h |
|
|
|
|
|
|
+1~-5 |
+1~-5 |
|
|
|
|
|
0~+1 |
0~+1 |
0~+1 |
1400℃×3h |
+1~-5 |
+1~-5 |
+1~-5 |
+1~-5 |
+1~-5 |
+1~-5 |
|
|
|
|
|
|
|
|
|
|
1300℃×3h |
|
|
|
|
|
|
|
|
|
|
+1~-5 |
+1~-5 |
+1~-5 |
|
|
|
1200℃×3h |
|
|
|
|
|
|
|
|
+1~-3 |
+1~-3 |
|
|
|
|
|
|
粘結時(shí)間(jiān) min |
1~3 |
1~3 |
1~3 |
1~3 |
1~3 |
1~3 |
1~3 |
1~3 |
1~3 |
1~3 |
1~3 |
1~3 |
1~3 |
1.5~2 |
1.5~2 |
1.5~2 |
粒度 % |
-1.0mm |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
|
|
|
根據用戶需要組織生(shēng)産 According to the requirement of customer to produce. |
+0.5mm |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
-0.074mm |
≥50 |
≥50 |
≥50 |
≥50 |
≥50 |
≥50 |
≥50 |
≥50 |
≥50 |
≥50 |
≥50 |
≥50 |
≥50 |
≥40 |
≥45 |
≥40 |
用途
|
用于砌築同材質耐火(huǒ)制(zhì)品
| | | |