 産品詳細介紹 |
|
項 目 \ 牌 号 |
EA98 |
EA90 |
EAM80 |
EM75 |
ESA75 |
ESA65 |
EA90CS |
EA90C |
EA90T |
EAM85T |
EA70T |
AZ28 |
| Al2O3 % |
≥98 |
≥90 |
≥80 |
≥75 |
≥75 |
≥65 |
≥90 |
≥90 |
≥90 |
≥85 |
≥70 |
≥50 |
| Fe2O3 % |
≤0.3 |
≤0.5 |
≤0.5 |
≤0.6 |
≤1.8 |
≤2.0 |
≤0.3 |
≤0.3 |
≤0.3 |
≤0.4 |
≤0.5 |
≤0.5 |
| ZrO2 % |
|
|
|
|
|
|
|
|
|
|
|
≥28 |
顯氣孔率 %
|
≤22 |
≤20 |
≤18 |
≤20 |
≤19 |
≤21 |
≤18 |
≤20 |
≤16 |
≤16 |
≤17 |
≤20 |
體(tǐ)積密度 g/cm3
|
≥3.0 |
≥2.85 |
≥2.70 |
≥2.55 |
≥2.65 |
≥2.5 |
≥2.90 |
≥2.85 |
≥2.95 |
≥2.60 |
≥2.50 |
≥3.15 |
常溫耐壓強度 Mpa
|
≥80 |
≥80 |
≥60 |
≥60 |
≥60 |
≥55 |
|
|
|
|
|
≥80 |
| 高(gāo)溫抗折 Mpa |
|
|
|
|
|
|
1500℃×0.5h
≥10 |
1450℃×0.5h
≥10 |
1500℃×0.5h
≥10 |
1450℃×0.5h
≥10 |
1400℃×0.5h
≥10 |
|
| 荷重軟化溫度 KD ℃ |
≥1700 |
≥1650 |
≥1650 |
≥1700 |
≥1520 |
≥1500 |
≥1700 |
≥1700 |
≥1700 |
≥1700 |
≥1650 |
T2≥1620 |
| 重燒線變化率 % |
1600℃×2h
±0.1 |
1600℃×2h
-0.1～+0.3 |
1500℃×2h
-0.1～+0.1 |
1500℃×2h
±0.1 |
1500℃×2h
0～+0.3 |
1500℃×2h
0～+0.3 |
|
|
|
|
|
|
| 熱震穩定性,次(1100℃ 水(shuǐ)冷) |
|
|
|
≥10 |
≥10 |
≥10 |
優 |
優 |
優 |
優 |
優 |
優 |
| 使用部位 |
爐底 |
滑軌 |
爐頂 |
側牆 |
側牆、爐頂、低(dī)滑區(qū) |
側牆、爐頂、低(dī)滑區(qū) |
高(gāo)溫
承接闆 |
低(dī)中溫承接闆 |
高(gāo)溫推闆 |
中溫推闆 |
低(dī)溫推闆 |
支撐拱頂 | | |
| |