 産品詳細介紹 |
|
項 目 \ 牌 号 |
CN-42 |
CN-40 |
CL-80 |
PZCL-78 |
CL-75 |
CL-65 |
CL-55 |
CL-80E |
CL-70E |
HA-60E |
HA-75E |
UH85K |
MA-A89 |
WMA-A92 |
| Al2O3 % |
≥42 |
≥40 |
≥80.0 |
≥78.0 |
≥75.0 |
≥65.0 |
≥55.0 |
≥80 |
≥70 |
≥60 |
≥75 |
≥85 |
≥86 |
≥92 |
| Fe2O3 % |
|
|
≤2.0 |
≤2.0 |
|
|
|
≤1.5 |
≤1.6 |
≤1.5 |
≤1.5 |
≤2.0 |
≤0.5 |
≤0.5 |
| TiO2 % |
|
|
|
|
|
|
|
|
≤3.5 |
|
|
|
|
≤0.1
|
| MgO % |
|
|
|
|
|
|
|
|
|
|
|
|
≥4.5 |
4-8 |
| SiO2 % |
|
|
|
|
|
|
|
|
|
|
|
|
≤2.5 |
≤0.5 |
| 耐火(huǒ)度 ℃ |
≥1760 |
≥1740 |
|
|
|
|
|
|
|
≥1850 |
≥1850 |
|
|
|
| 荷重軟化溫度KD ℃ |
≥1430 |
≥1400 |
≥1530 |
≥1550 |
≥1510 |
≥1490 |
≥1470 |
T2≥1550 |
T2≥1520 |
T2≥1600 |
T2≥1650 |
T2≥1500 |
T2≥1650 |
T0.5≥1550 |
| 高(gāo)溫抗折1500 ℃ MPa |
|
|
|
|
|
|
|
|
|
|
|
|
|
≥2.0 |
| 重燒線變化率 % |
1400℃×2h
0～-0.3 |
1400℃×2h
0～-0.3 |
1550℃×2h
0.1～-0.5 |
1550℃×2h
0.4～-0.3 |
1500℃×2h
0.1～-0.5 |
1500℃×2h
0.1～-0.5 |
1450℃×2h
0.1～-0.5 |
1500℃×2h
-0.1～+0.5 |
1500℃×2h
-0.1～+0.5 |
1500℃×2h
0～+1.0 |
1500℃×2h
0～+1.0 |
1500℃×5h
>+0.5 |
1600℃×3h
0～+0.5 |
1500℃×5h
-0.3～+0.3 |
| 顯氣孔率 % |
≤18 |
≤19 |
≤24 |
≤21 |
≤28 |
≤28 |
≤22 |
≤19 |
≤20 |
≤17 |
≤19 |
≤19 |
≤19 |
≤22 |
| 體(tǐ)積密度 g/cm3 |
|
|
|
|
|
|
|
≥2.75 |
≥2.5 |
≥2.60 |
≥2.65 |
≥2.80 |
≥3.0 |
≥3.05 |
| 常溫耐壓強度 Mpa |
≥39.2 |
≥34.3 |
≥50 |
≥70 |
≥40 |
≥35 |
≥45 |
≥60 |
≥60 |
≥60 |
≥60 |
≥50 |
≥60 |
≥40 | | | |