 産品詳細介紹 |
|
項 目 \ 牌 号 |
鋁鎂澆注料 |
鋁尖晶石
澆注料
|
鎂鈣質噴補料 |
中間(jiān)包塗料
|
中間(jiān)包鎂鈣質幹式振動料
|
穩流器(qì)
|
|
MPL-1 |
MPL-2 |
MD |
MGD |
Al2O3 %
|
≥70
|
≥72
|
|
|
|
|
|
|
| MgO % |
≥9 |
≥10 |
75-80 |
70-80 |
60-85 |
50-85 |
50-70 |
≥75 |
| CaO % |
|
|
5-10 |
2-10 |
|
|
|
≤6.0 |
| SiO2 % |
≤10
|
≤9
|
≤4
|
≤10
|
|
|
|
SiO2+Fe2O3
+Al2O3 ≤10 |
| 耐火(huǒ)度 ℃ |
|
|
≥1790 |
≥1790 |
|
|
|
|
體(tǐ)積密度 g/cm3
|
|
|
|
|
>2.0
|
|
|
≥2.85 |
抗折強度 Mpa
|
110℃×24h
|
≥8
|
≥11.5
|
|
|
|
|
|
|
1500℃×3h
|
≥13
|
≥11.5
|
|
|
|
|
|
|
耐壓強度 Mpa
|
110℃×24h
|
≥60 |
≥90 |
|
|
>5.0 |
|
|
≥80 |
| 1500℃×3h |
≥80 |
≥100 |
|
|
>8.0 |
>8.0 |
>8.0 |
|
燒後線變化率%
|
1500℃×2h |
-0.1～0.2 |
-0.2～0.35 |
|
|
1500℃×3h
-2.5～-1.0 |
|
|
|
| 粒度 mm |
|
|
|
|
<3 |
|
|
|
| 使用壽命 小(xiǎo)時(shí) |
|
|
|
|
10-40 |
10-60 |
10-40 |
| | | | |